Evaluation of Natural Oil Adducts in Alkyd-Based Varnish Emulsion and Effect on Rowan (Sorbus torminalis) Wood
Asian Journal of Biotechnology and Bioresource Technology,
In these days, preparation of eco-friendly wood surface coating agents has become important topic for environmental concerns. In this study, an alternative surface coating formulations was prepared with adducts of oils of apricot kernel (A), sesame (S) and grape seed (G) were mixed with oil modified alkyd-based synthetic varnish system. These emulsions were applied on Rowan (Sorbus torminalis) wood and exposed artificial UV irradiation. However, all emulsion coated samples show lower water sorptions regardless of conditions or level of treatments. Increasing adduct charges from 5.0% to 10% have not considerably effects for water sorptions. The reducing water sorption properties of 35.5%, 35.2% and 39.4% were obtained with 10% sesame oil-varnish coated samples of 10Sı and 10 Sıı in one- and two-time coatings and three-times coated samples of 5Sııı in 5.0% sesame oil-varnish emulsion coatings, respectively. Moreover, selected oil adducts into varnish had one and two point lowering effects on coated surface hardness (in 4H-5H levels). The UV exposure seems to not much influence on surface hardness properties. The similar tendency were also observed for cross-cut resistance that marginally similar adhesion (scratch resistance) for both control and UV exposured samples. Increasing coatings and charge of apricot kernel oil in varnish emulsion looks like more effective than other varnish formulations, in terms of gloss stability. However, increasing adducts charges and UV radiation time, have more less similar effects on all coated and UV irradiated samples.
- water sorption
- pencil hardness
- surface scratch resistance
How to Cite
Feist W. The outdoor finish, how and when to paint or stain, Fine hausebuilding, pp. 54-55.1985.
Cassens D, Feist, W. Exterior wood in south, selections applications and finishes. USDA Forest Service. FPL-GTR-69. Madison, WI. USA; 1991.
Sahin HT, Arslan MB, Korkut S, Sahin C. Colour changes of heat‐treated woods of red‐bud maple, European hophornbeam and oak. Color Research & Application. 2011;36(6):462-466.
Sahin CK, Topay M, Var AA. A study on suitability of some wood species for landscape applications: surface color, hardness and roughness changes at outdoor conditions. Wood Research. 2020;65(3):395-404.
Sadiki M, Elabed S, Barkai H, Balouiri M, Nasri A, Koraichi SI. The modification of cedar wood surface properties for the prevention of fungal adhesion. International Journal of Adhesion and Adhesives. 2017;75:40-46.
Sahin HT, Mantanis GI. Colour changes in wood surfaces modified by a nanoparticulate based treatment. Wood research. 2011;56(4):525-532.
Papadopoulos AN, Taghiyari HR. Innovative wood surface treatments based onnanotechnology, Coatings. 2019;9(12):866.
Sahin HT, Erbil I. A study on surface physicochemical properties of woods treated in emulsion of waterborne varnish with sesame and grape seed oil. Asian Journal of Biotechnology and Bioresource Technology. 2021;7(1):1-9.
González-Laredo RF, Rosales-Castro M, Rocha-Guzmán NE, Gallegos-Infante JA, Moreno-Jiménez MR, Karchesy JJ. Wood preservation using natural products. Madera y Bosques. 2015;21:63-76.
Sadiki M, Elabed S, Barkai H, Laachari F, Koraichi SI. The impact of Thymus vulgaris extractives on cedar wood surface energy: Theoretical and experimental of Penicillium spores adhesion. Industrial Crops and Products. 2015;77:1020-1027.
Sadiki M, Barkai H, Ibnsouda Koraichi S, Elabed S. The effect of the Thymus vulgaris extracts on the physicochemical characteristics of cedar wood using angle contact measurement. Journal of Adhesion Science and Technology. 2014;28 (19):1925-1934.
Goktas O, Duru ME, Yeniocak M, Ozen E. Determination of the color stability of an environmentally friendly wood stain derived from laurel (Laurus nobilis L.) leaf extracts under UV exposure. Forest Products Journal. 2008;58.
Goktas O, Ozen E, Duru ME, Mammadov R. Determination of the color stability of an environmentally-friendly wood stain derived from oleander (Nerium oleander L.) leaf extracts under UV exposure. Wood Research. 2009;54(2):63-72.
Özen E, Yeniocak M, Colak M, Goktas O, Koca İ. Colorability of wood material with Punica granatum and Morus nigra extracts. Bio Resources. 2014;9(2):2797-2807.
Alpaslan M, Hayta M. Apricot kernel: Physical and chemical properties. J. Amer. Oil Chem. Soc., 2006;83(5):469.
Anonymous. Susam yağı. Accesses: 10 July, 2020.
Koç M. Determination of physicochemical properties and oxidative stability of seed oils of different grape varieties obtained by cold pressing technique (Turkish, Abstract in English) (MSc thesis), Namık Kemal University, Graduate School of Natural and Applied Sciences, Department of Food Engineering, Hatay. 2016; 62.
Sevindik A, Selli S. Main bioactive compounds of grape seeds, Çukurova J. Agric. Food Sci. 2016;31(2): 9-16. Turkish.
ISO 2813:2014. Paints and Varnishes-Determination of Gloss Value at 20◦ , 60◦ and 85◦ ; ISO: Geneva, Switzerland, 2014.
ASTM D3363: Standard test method for film hardness by pencil test, ASTM ınternational, West Conshohocken, PA, USA.
ISO 2409:2020. Paints and varnishes-Cross-cut test; ISO: Geneva, Switzerland; 2020.
Ye L, Banach S, Arney J. Interpretation of gloss meter measurements. Journal of Imaging Science and Technology. 2006;50(6):567-571.
Abstract View: 195 times
PDF Download: 82 times